A water-based, three-component, polyurethane-cement mortar with a liquid consistency. It creates a highly effective smooth floor 4-6 mm thick and is highly resistant to abrasion, impact and chemical attack.

Features

• high mechanical parameters, excellent compressive strength, abrasion, impact strength, mechanical cleaning, wear, etc.
• excellent chemical resistance, better than epoxy system
• good thermal resistance from -25 C to +70 C
• material quick-drying circular motion already possible after 48 hours from application
• liquid consistency and very good workability allow to obtain a smooth surface quickly and easily
• creates an uninterrupted coating without structural joints
• environmentally friendly product, non-toxic, solvent-free, non-flammable, suitable for use in rooms with low air movement

Application

• surfaces with heavy vehicle traffic, in rooms with difficult operating conditions
• in industrial environments on substrates requiring very high chemical resistance to cleaning substances, degreasing surfactants, fats, diluted acids and bases, hydrocarbons and other aggressive substances
• smooth-surface floors in the petrochemical, pharmaceutical, food, etc. industries, which impose very high requirements on the materials used in terms of mechanical and chemical resistance

Technical data

• component density in A / B / C 0.99 / 1.23 / 1.50 0.10 g / cm ³
• density of A + B + C fresh mix 1.97 0.10 g / cm ³
• density of the mature product and after drying 1.85 0.10 g / cm ³
• minimum application temperature of substrate and surroundings> 5 ° C
• pot life at 20 ° C 20 min
• initial / final setting time at 20 ° C 1-2 / 3-4 h
• complete solidification time at 20 ° C and 50% relative humidity before putting into service for: pedestrian traffic 12 days; moderate vehicular traffic 24 days; heavy traffic 48 days
• compressive strength after 28 days> 35 N / mm ² (according to EN 13892-2)
• bending strength after 28 days> 10 N / mm ² (according to EN 13892-2)
• adhesion to concrete after 28 days> 3 N / mm ² (EN 13892-8)
• (breaking concrete)
• thermal resistance of a 4-5 mm thick layer from -15 C to +50 C; > 5-6 mm from -30 C to +60 C (occasionally up to +70 C)
• one layer thickness 4-6 mm
• consumption * per one layer 2.0 kg / m mm
• packaging: a set of 35.70 kg

* actual consumption is indicative and varies depending on the porosity, texture and condition of the substrate and the application method used