Three-component, self-leveling cement-based mortar, modified with water-borne epoxy resins.

Features

• self-leveling
• its fluidity ensures quick and simple application
• does not require any primer - primer
• good adhesion to concrete substrates, even mat-damp
• allows the substrate to breathe, being a vapor-permeable material
• anti-skid finish by sprinkling with quartz sand while the material is still fresh
• does not attack reinforcement
• waterproof

Application

• Self-leveling mortar for finishing floors with a thickness of 1.5 mm to 3 mm
• finishing floors in industrial halls, parking lots, water reservoirs
• repairing a hole in the floor by adding quartz sand

Technical data

• color and appearance: component A milky liquid; component B light liquid; component C white and gray powder
• mixture density 2.0 0.05 g / cm ²
• consumption time of the prepared material (20 C) 20 min
• minimum application temperature> 8 ° C
• maturing / handing over time for pedestrian traffic (20 C) 24 h
• compressive strength after 28 days 30 MPa
• bending strength after 28 days 7 MPa
• surface hardening SH 88.4 N / mm ²
• impact resistance 7.85 / 800 N m / mm
• abrasion resistance according to Taber 500/1000 cycles 4.4 / 2.2
• Bohm abrasion resistance 4.5 cm3 / 50 cm ²
• adhesion to concrete after 28 days> 2.5 MPa
• chemical resistance to sewage, sea water, salts, industrial oil, fats very good
• approximate consumption of clean / with sand 2.25 / 1.7 kg / m ² / mm
• minimum and maximum thickness of clean / with sand 1.5–3 / 3-8 mm
• package 30.55 kg